Abstract
AbstractA melt‐mixing procedure has been used to disperse multi‐walled carbon nanotubes (MWCNT) in an epoxy matrix. According to dynamic viscoelastic results, a physical network is formed for carbon nanotube concentrations of 0.3 weight per cent (wt%) and above. The temperature activated curing process is followed analyzing the evolution of the dynamic viscoelastic functions and the dielectric loss with time. Curing process from a physical to a chemical network is monitored. The presence of MWCNT accelerates curing, even when the rheological percolation is not reached (absence of physical network). Several hypotheses are considered to explain this result. Electrical conductivity decreases during cure, so lower electrical conductivities are found for cured MWCNT/epoxy samples than for dispersions: this is explained by a distortion of nanotubes physical network and a reduction of the ionic conductivity contribution of the liquid phase. POLYM. ENG. SCI., 2012. © 2011 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.