Abstract
Acrylonitrile‐butadiene rubber (NBR) composites filled with co‐precipitates of black liquor and montmorillonite (CLM) were prepared by mechanical mixing on a two‐roll mill. The cure characteristics, mechanical properties, thermal properties, and thermo‐oxidative aging properties of NBR/CLM composites were evaluated. Scanning electron microscopy and transmission electron microscopy showed that the filler particles were well dispersed in the NBR/CLM composites. The scorch time and optimum cure time increase with increasing filler loading. A remarkable enhancement in tensile strength, elongation at break, 300% modulus, and shore “A” hardness was also observed. When the loading of CLM was 40 parts per hundred rubbers, it showed about seven times increase in tensile strength, about 1.8 times increase in elongation at break, about three times increase in 300% modulus, and about 1.3 times increase in shore A hardness, respectively, as compared with those of pure cured NBR. Thermal properties and thermal oxidative aging properties, in general, were also improved with loading of this novel filler. Copyright © 2011 John Wiley & Sons, Ltd.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.