Abstract
To enable the comprehensive application of Al2O3-Cr2O3 solid solutions, the crystal structures and properties of Al2O3-Cr2O3 solid solutions with different Cr2O3 contents were studied. It was observed that Al2O3 and Cr2O3 form a complete substitutional solid solution over the entire composition range at 1650°C, with no compounds being formed. Lattice parameters “a” and “c” both increase linearly with an increase in the Cr2O3 content. The doping of the Cr3+ ions causes a more severe lattice strain in the c-axis direction. The diffraction angles of the diffraction peaks decrease in a linear manner with the increase in the Cr2O3 content. The relationship between the theoretical density of the solid solution and the Cr2O3 content could be fitted using a second-order polynomial. It was also observed that the linear expansion coefficient of the solid solutions decreases with an increase in the Cr2O3 content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.