Abstract
Au/NiCr/Ta soft multi-layered metal films were deposited on hard Si-(111) substrate by magnetron sputtering. The crystal orientation, Hardness (H) and Elastic modulus (E) were investigated as a function of substrate temperature by XRD and nanoindentation techniques. The XRD revealed that all films on Si-(111) substrate are Au-(111) preferred orientation, indicating there are no alloying phases in the films, which is different from Au/NiCr/Ta films on Al2O3 substrate with a mixture of Au-(111) and Au-(200) orientation. Nanoindentation tests at shallow indentation depths (h≤t/4) where the hardness is reliable for metal films on hard substrate. Au film at substrate temperature 200°C has the highest hardness 4.2GPa. Meanwhile, the H/E value also indicated that the Au/NiCr/Ta films have preferable wear resistance at substrate temperature 200°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.