Abstract
In order to investigate the effect of frequency on the crack growth behavior, ultrasonic fatigue tests were carried out for an extruded age-hardened Al alloy, 7075-T 6, in ambient air and in N2 gas, and the results were compared with those in rotating bending fatigue. Fatigue strength was higher in ultrasonic fatigue than in rotating bending one. This was caused by the retardation of a crack initiation and its early propagation. In ultrasonic fatigue, the growth direction of a crack changed macroscopically from a tensile mode to a shear one which the direction was about 35 degrees against to the specimen axis, and fracture mechanism also changed from striations to transgranular facets with voids microscopically. Crack growth rate at the transition of crack growth direction was about 3 × 10-9 m/cycle. The relation between an applied stress σa and a crack depth at the transition of crack growth direction bT was expressed by σnabT=constant. These results were explained from the time dependent environmental effect and texture of microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.