Abstract
This paper examines the corrosion resistance of 08Kh22N6T and 08Kh21N6M2T steels which would make it possible to ensure equal properties of all the zones of the welded joints. The investigations were carried out on the welded joints in the steels produced with new OZL-40 and OZL-41 electrodes and with standard TsL-11 and EA-400/10u electrodes. The chemical compositions of the steels and deposited metal are presented. The tests of the intercrystalline corrosion resistances of the welded joints in the steels in the as-welded condition and after heat treatment showed that the weld metal is not attacked by intercrystalline corrosion. The tests also showed that the welded joints in 08Kh22N6T steel made with the OZL-40 and TsL-11 electrodes are resistant to corrosion in 55% phosphoric acid at 90 C in 1% sulfuric acid, and in 25% formic acid at 80 C. The investigated steels made with the OZL-40 and OZL-41 electrode respectively show that the welded joints are resistant to intercrystalline and general corrosion, have high mechanical and processing properties and the electrodes, and can be used for welding equipment designed for service in alkaline, neutral, and slightly acid media.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.