Abstract
The present study reports on the corrosion fatigue behavior of ultrafine-grained (UFG) Niobium 2 wt-% Zirconium (NbZr) alloy in simulated body fluid (SBF). The alloy was processed using multipass equal channel angular processing at room temperature, resulting in a favorable combination of high strength and ductility along with superior biocompatibility and excellent corrosion resistance. Electrochemical measurements revealed stable passive behavior in SBF saline solutions, similar to conventional Ti–6Al–4V alloy. High-cycle fatigue tests showed no alteration in the crack initiation behavior due to the SBF environment, and an absence of pitting and corrosion products. More severe test conditions were obtained in the fatigue crack growth experiments in saline environments. Crack growth rates in UFG NbZr were marginally increased in SBF as compared to laboratory air at a constant test frequency of 20 Hz. Upon a 100 fold decrease in the test frequency, slightly higher crack growth rates were observed only in the near-threshold region. Such excellent corrosion and corrosion fatigue properties of UFG NbZr recommend it as an attractive new material for biomedical implants.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.