Abstract
Poor corrosion and wear resistance of magnesium (Mg) alloys restrict their applications. Herein, corrosion and wear‐resistant films are formed upon Mg alloy AZ31 through a micro‐arc oxidation (MAO) process in silicate electrolyte in the presence of carbon spheres (CS). Surface morphology, chemical composition, corrosion resistance, hardness, and coefficient of friction (CoF) of the MAO coatings are investigated using field‐emission scanning electron microscopy (FE‐SEM), Fourier transform infrared spectrometry (FTIR), X‐ray diffractometer (XRD), X‐ray photoelectron spectroscopy (XPS), electrochemical and hydrogen evolution measurements, automatic micro‐hardness testing, and reciprocating tribometer, respectively. Results demonstrate that the surface morphology and hardness of MAO coatings vary with the concentration of CS. The presence of CS results in an increased coating thickness from 8.0 ± 1.8 to 12.2 ± 1.8 μm, mean pore size from 0.7 ± 0.1 to 1.9 ± 0.1 μm, open porosity of MAO coating from 4.2 ± 0.4 to 5.6% ± 1.1%, and coating hardness from 347.0 ± 59.0 to 853.0 ± 67.3 Vickers‐hardness (HV). Furthermore, CS‐modified MAO coatings lead to improved corrosion resistance in comparison with that of the neat MAO counterparts. Moreover, the high hardness and formation of SiC of CS‐modified coatings lead to a low and stabilized CoF, which implies an enhanced wear resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.