Abstract
An intergranular corrosion is a main degradation mechanism of austenitic stainless steels for use in a nuclear fuel reprocessing plant. The intergranular corrosion is caused by the segregation of impurities to grain boundaries and the resultant formation of active sites. Extra High Purity (EHP) austenitic stainless steel was developed with conducting the new multiple refined melting in order to suppress the total harmful impurities less than 100ppm. The intergranular corrosion behavior of EHP austenitic stainless steels added various impurities was examined in boiling HNO3 solution with highly oxidizing ions to find a correlation between the intergranular corrosion and the impurities of EHP-SSs. The corrosion rate of EHP austenitic stainless steels supported with the degree of intergranular corrosion relatively well. The relationships between the corrosion rate and the impurities content for EHP-SSs was determined using a multiple regression analysis. The influence on corrosion rate became small in order of B, P, Si, C, S and Mn. There is little effect of Mn on corrosion rate of EHP-SSs in case of 10000appm or less. It was important to control B and P in intergranular corrosion behavior of EHP-SSs
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.