Abstract
The paper presents the effect of electron beam alloying on the surface of a copper flat bar (M1Ez4) with titanium powder. Due to the quality of the surface after alloying and the obtained properties, the parameters used were given which met the assumed conditions to the greatest extent. The microstructure and mechanical properties as well as the chemical composition of surface-modified electron-beam copper show improved mechanical properties, i.e. hardness and abrasion resistance. This article uses research techniques using scanning electron microscopy and analysis of chemical composition in micro-areas (EDS). In order to examine the properties of the material after electron beam modification, hardness measurements were performed at low loads (HV0.1), abrasion resistance was tested, and conductivity was also measured. As a result of modifying the chemical and phase composition of M1E copper using an electron beam, the hardness increased by 46%, while the conductivity decreased by 16% due to the formation of intermetallic phases during solidification.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.