Abstract
Through a seed-mediated growth route, Pt nanoparticles (NPs) with tunable shape and size were prepared, such as octahedral, cuboctahedral, branched and rice-like. Three nanometer Pt NPs were prepared and dispersed in oleyl amine to form seed solution and then Pt precursor (platinum acetylacetonate (Pt(acac)(2))) was added. Under high temperature, oleyl amine as both reducing and protective agents can reduce Pt precursor to Pt atoms which selectively deposit on seeds surface to form variously structured Pt NPs. By adjusting the reactive conditions (the molar ratio of Pt metals from Pt(acac)(2) and seed (PPS), the seed diameter, the addition route of Pt(acac)(2)), the NPs growth could be controlled to fall into kinetic or thermodynamic regime, producing variously shaped NPs. On the basis of observed results, a reaction mechanism in which the resulting NP shape had strong dependence on c/s (c=precursor concentration, s=available deposition surface area) was figured out. The obtained NPs were supported on black carbon to act as Pt/C catalysts for oxidization of methanol and results show that the catalysts from branched NPs had higher catalytic activity and stability than ones from polyhedral NPs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.