Abstract
Three microporous coordination polymers, namely, [Co2L(DPE)]·2DMF·5H2O (1), [Zn2L(DPE)]·2.5DMF·2H2O (2) and [Cd(H2L)]·3DMF·3.5H2O (3), were solvothermally prepared in the presence of the flexible tetrahedral carboxylate ligand tetrakis[(4-carboxyphenyl)oxamethyl]methane acid (H4L) and a secondary bidentate linker (E)-1,2-di(pyridin-4-yl)ethane (DPE). Compounds 1 and 2 are isostructural and possess a 2-fold interpenetrating (4,4)-pts network. Compound 3 has a 3D structure with a uninodal 4-connected {4.85} topology. All the three compounds consist of large solvent-accessible voids, but only compounds 1 and 2 possess permanent porosity as confirmed by N2, CO2 and CH4 gas adsorption measurements. In addition, compounds 2 and 3 exhibited strong photoluminescent emissions at room temperature with a peak at 495 and 440 nm, respectively, owing to a ligand-centered excited state. The emission intensities of 2 varied upon contact with different solvents or analytes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.