Conducting nanocomposites of polyacrylamide with acetylene black and polyaniline

Abstract

AbstractA conducting nanocomposite of polyacrylamide (PAA) with acetylene black was prepared via Na2AsO3‐K2CrO4 redox initiated polymerization of acrylamide in water containing a suspension of acetylene black. FTIR analyses confirmed the presence of PAA in the nanocomposites. The composite possessed lower thermal stability than AB and exhibited three stages of decomposition upto 430°C. DSC thermogram revealed three endotherms due to minor thermal degradation (at ∼100°C), melting and decomposition (at ∼230°C) and major decomposition (at ∼430°C). TEM analyses indicated the formation of globular composite particles with sizes in 30–70 nm range. In contrast to the very low conductivity of the base polymer the composite showed a dramatic increase in conductivity (0.19–6.0 S/cm) depending upon AB loading. Log (conductivity) –1/T plot showed a change in slope at ∼127°C indicating the manifestation of an intrinsic conductivity region and an impurity conductivity region. The activation energy for conduction as estimated from the slope of region I was 0.008 eV/mol. The C–V plot was linear showing a metallic behavior. For comparison in conductivity PAA‐polyaniline composite was also prepared which however displayed much lower conductivity values. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers