AbstractWe have used x-ray microbeam fluorescence and diffraction for in-situ measurements of electromigration-induced Cu diffusion and stress evolution in passivated, polycrystalline 10[.proportional]m-wide, 200[.proportional]m-long Al(0.25 at.% Cu) conductor lines. Cu migration is in the direction of the electron flow and is determined by the direction and magnitude of the current and by the temperature during electromigration. The effective charge and diffusivity of Cu in Al(Cu) have been obtained from analysis of the Cu concentration profiles. The evolution of electromigration-induced strains normal to the sample surface has been monitored by x-ray microbeam diffraction. A linear strain profile developed after about 9 hrs of electromigration with 1.5[.dotmath]105 A/cm2 at 300°C, corresponding to 3MPa/[.proportional]m equi-biaxial stress. From the Cu profile measured at the same time, the critical Cu concentration for significantly slowing down Al grain boundary diffusion is estimated to be ∼0.15 at. %. These data also confirm that downstream Cu transport is accompanied by a counter flow of Al in the upstream direction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.