Abstract
Temperature and power dependent photoluminescence (PL) measurements were employed in order to study defects in close-space-sublimation grown polycrystalline cadmium telluride layers that had been activated with different chlorine containing compounds. The samples were either measured as-grown or after thermal treatment in an oxygen containing ambient with and without the chlorine containing compounds such as cadmium chloride, hydrochloric acid, and sodium chloride. The as-grown sample is discussed in detail, in order to then demonstrate the changes in the PL spectra induced by the postdeposition treatments. A deep level transition at 1.32 eV was observed in the as-grown sample which can be correlated with cadmium vacancies. Due to postdeposition treatments this deep level transition disappears and a broad band correlated with A-centers arises instead at about 1.43 eV. Another transition band at 1.479 eV in the as-grown sample is not influenced by any postdeposition treatment. Furthermore, by processing solar cells out of the respective samples, the PL results can be related to the solar cell parameters.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.