Color stability and hardness in dental composites after accelerated aging

Abstract

Objectives. To investigate the color and microhardness changes of five chemically- and five light-curing composites as a function of accelerated aging from light exposure. Materials and methods. From each material five composite specimens were embedded in epoxy resin prior to determining the Knoop microhardness of the surface. For analyzing the color ΔE ∗=f((L ∗a ∗b ∗)) with a spectrophotometer, three discs per composite were prepared. After measuring the baseline for hardness and color the same specimens were exposed to a xenon arc light and water in a Weather-Ometer machine for a total radiant energy of 150 kJ/m 2 and 122 h. The microhardness and the color were again determined following the aging treatment. Results. Each material showed a significant increase in hardness after aging treatment ( p<0.05). Comparing the hardness changes (in %) of the light-cured materials with the chemically cured materials, no significant difference could be found. Perceptible color differences could be observed for all the materials. Three brands showed small differences with ΔE ∗=1.6–2.2, while four composites had ΔE ∗ ranging from 6.2 to 15.5. A significant correlation between hardness values and color changes could not be established. Clinical significance. The findings suggest that, since light-curable materials showed significantly more resistance to color changes after accelerated aging by light and water than chemically-cured materials, they may be more esthetically acceptable. Color changes were not correlated with surface hardness changes of the materials after aging.