Abstract
TiO2 -based photoanodes have attracted extensive attention worldwide for photoelectrochemical (PEC) water splitting, but these materials still suffer from poor electron-hole separation and low photoconversion efficiency. Here, the high PEC water splitting activity and long-term stability against photocorrosion of well-aligned hierarchical TiO2 @CoNi-layered double hydroxides nanotube arrays (TiO2 @CoNi-LDHs NTAs) are reported. The typical TiO2 @CoNi-LDHs NTAs exhibits enhancing photocurrent density of 4.4 mA cm-2 at a potential of 1.23 V (vs reversible hydrogen electrode) under AM 1.5G simulated sunlight (100 mW cm-2 ), 3.3 times higher than that of the pristine TiO2 sample. Moreover, this hierarchical electrode displays excellent stability against photocorrosion with initial activity loss no more than 1.0% even after 10 h irradiation in Na2 SO4 electrolyte solution (pH 6.8), much competitive to those reported TiO2 -based photoelectrodes. This work may offer a combinatorial synthesis strategy for the preparation of hierarchical architectures with high PEC performances.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.