Abstract
Studies have shown that enamel can be modified by pulsed CO2 laser to form a more acid-resistant substrate. This study evaluated the effects of a 10.6-microm CO2 laser on enamel surface morphology and chemical composition as well as monitored intrapulpal temperature changes during irradiation. Human teeth were irradiated with fluences of 1.5-11.5 J/cm2, and pulpal thermal as well as chemical and morphological modifications on enamel were assessed. The teeth were submitted to a pH-cycling model, and the mineral loss was determined by means of cross-sectional microhardness. For all irradiated groups, intrapulpal temperature changes were below 3 degrees C. FT-Raman spectroscopy and scanning electron microscopy indicated that fluences as low as 6.0 J/cm2 were sufficient to induce chemical and morphological changes in enamel. Then, for fluences reaching or exceeding 10.0 J/cm2, laser-induced inhibitory effects on demineralization were observed. It was thus concluded that laser energy density in the range of 10.0 and 11.5 J/cm2 could be applied to dental enamel in order to produce chemical and morphological changes and reduce the acid reactivity of enamel without compromising the pulp vitality.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.