Abstract
Passivity degradation of 304 stainless steel (SS) in simulated alkaline water chemistries at 300°C was investigated using polarization curve, scanning electron microscope, time-of-flight secondary ion mass spectrometry (SIMS) and X-ray photoelectron spectroscopy (XPS). Experimental results indicated that 304, SS was selfpassive in the test solution and the thickness of passive film was about 500 nm. Hydroxide was enriched in the outer layer whereas oxide was enriched in the inner layer. Sulfur in thiosulfate could be reduced into lower valence of sulfur and enter the passive film so that the composition of passive film was modified by sulfur. Fe and Cr were enriched in the passive film whereas Ni was depleted in the passive film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.