Abstract
The hot deformation behavior of Ti-4.5Al-3V-2Mo-2Fe (SP-700) titanium alloy in the temperature range of 650°C~950°C and constant strain rate of 0.01, 0.1, 1 and 10s-1 has been investigated by hot compressive testing on the Gleeble-1500D thermal simulation test machine. The experimental results indicated that the hot deformation behavior of SP-700 alloy was sensitive to the deformation temperature and strain rate. The peak flow stress decreased with the increase of temperature and the decrease of strain rate. The flow curves characteristic under different deformation parameters show significant different. Analysis of the flow stress dependence on strain rate and temperature gives a stress exponent of n as 4.8235 and a deformation activation energy of Q as 410kJ/mol. Based on the dynamic materials model, the processing map is generated, which shows that the most peak efficiency domain appears at the temperature of 725°C~775°C and the strain rate of 0.001 s-1~0.003s-1 with a peak efficiency of 45% at about 750°C/0.01s-1.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.