Abstract
LiMn2O4 thin films were prepared by solution deposition using lithium acetate and manganese acetate as raw materials. The phase constitution and surface morphology were observed by X-ray diffraction and scanning electron microscopy. The electrochemical properties of the thin films were studied by cyclic voltammetry, charge-discharge experiments and impedance spectroscopy in 1 mol·L−1 LiPE6/EC-DMC solution using lithium metal as both the counter and reference electrodes. The films prepared by this method are of spinel phase. The lattice parameter increases with the annealing temperature and annealing time. The film annealed at 750°C for 30 minutes has the highest capacity of 34.5 μAh·cm−2·μm−1, and its capacity loss per cycle is 0.05% after being cycled 100 times.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.