Abstract
Nitrogen (N) doped TiO2 supported vanadium phosphorus oxide (VPO) catalysts were prepared and tested for catalytic oxidation of NO. The experimental results showed that 0.1V(5)PO/TiN(1) was the optimal catalyst for NO oxidation and the NO conversion could reach 61% at temperature of 350°C. The physico–chemical properties of 0.1V(5)PO/TiN(1) catalyst were characterized by Brunauer–Emmett–Teller measurements (BET), Photoluminescence (PL), X–ray photoelectron spectroscopy (XPS), Infrared spectroscopy measurements of NH3 adsorbed on catalysts (NH3–IR), and Infrared Fourier transform spectroscopy (FTIR). The PL and XPS spectra revealed that the oxygen storage capacity and catalytic activity of VPO/Ti catalyst can be improved by nitrogen doping. The H2–TPR profile also indicated that V(5)PO/TiN(1) catalyst had a superior redox property. Activity test results and FTIR spectra showed that 0.1V(5)PO/TiN(1) catalysts had a superior resistivity to SO2 and the NO oxidation rate is above 50% at temperature of 350°C when SO2 concentration is 200ppm to 800ppm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.