Abstract
To establish the most effective cementation protocol for bonding zirconia crowns to Ti-Base CAD/CAM abutments in terms of abutment height, cement type, and surface pretreatment. Zirconia crowns were designed to fit abutments of 2.5-mm (short) and 4.0-mm (tall) height. The retention of conventional resin cement with a universal adhesive (RelyX Ultimate, 3M ESPE) was compared to self-adhesive resin cement (RelyX U200, 3M ESPE) following different surface pretreatments (n = 10/group): (1) no treatment (NT); (2) Ti-Base abutment surface blasting with alumina particles (SB); (3) zirconia crown tribochemical surface blasting with silica-coated alumina particles (TBS); and (4) a combination of SB + TBS. Pull-out testing was performed in a universal testing machine. Data were statistically evaluated using a linear mixed model following least significant difference post hoc test. Pull-out data as a function of Ti-Base height demonstrated higher retention for tall compared to short abutments (P < .001). Ultimate outperformed U200 cement (data collapsed over height and pretreatment) (P < .001). Analysis of pretreatment depicted higher retention for SB + TBS, followed by SB, TBS, and NT (P < .04). The interaction between Ti-Base height and cement type highlighted the superior adhesive strength of Ultimate compared to U200 for both heights (P < .001). Irrespective of type of pretreatment, surface pretreatment improved the retention for U200 cement and short Ti-Base (P < .03 compared to NT). In contrast, higher retention was demonstrated for SB + TBS, followed by SB, TBS, and NT, for Ultimate cement combined with tall Ti-Base (P < .02) (data collapsed over height and cement, respectively). There was a direct relationship among Ti-Base height, micromechanical and/or chemical pretreatment, and conventional adhesive bonding in improving the retention of zirconia crowns.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.