Abstract
The cavitation erosion resistance of non-nitrided and low plasma nitrided AISI 410 martensitic stainless steel was evaluated according to ASTM G32 standard. Plasma nitriding was carried out in a hot wall DC-pulsed plasma reactor at 400°C in a mixture of 75% of nitrogen and 25% of hydrogen during 20h. The ASTM A 743 grade CA6NM stainless steel was used for comparison purposes. The microstructure of the steels was characterized by optical and scanning electron microscopy, as well as by X-ray diffraction. Expanded martensite and iron nitrides were formed at the surface of the martensitic AISI 410 stainless steel. Curves of mass loss, erosion rate and roughness parameters were plotted as a function of exposure time. The 25μm thick nitride layer showed two distinct regions: a first 5μm thick layer just beneath the surface containing precipitated ε Fe3N nitrides and expanded martensite and the rest of the layer constituted solely by expanded martensite. Iron nitride precipitation drastically reduced the incubation period, allowing detachment of entire grains due to the impact of shock-waves over the surface. Despite this, after removal of the first 5μm thick layer, the cavitation erosion resistance improved significantly. The relationship between microstructure and time-variation curves and wear mechanisms are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.