Abstract
We used solid-condition processes to make a sequence of radiation-adjustable phosphors Eu2+/Mn2+ co-doped Ca9La(PO4)7 (shortened as CaLa:EM), which show a consistently variable hue from green to yellow and red via an efficient resonance-form energy transition as well as the strength of green and red radiations may be controllable through altering the Mn2+concentration. We examined the transition of energy (Eu2+®Mn2+) for CaLa:EM. It is proved to be a resonant kind using a dipole-quadrupole process, having power shift critical range calculated to be 11.36 Å by using the spectral overlap techniques. Mixing a 365 nm UV-InGaN chip as well as one phosphor combination containing (Ca0.98Eu0.005Mn0.015)9La(PO4)7 in yellow with BaMgAl10O17:Eu2+in blue produced a warming WLED having CIE color coordinates measured at (0.35, 0.31), better CRI value (Ra)measured at 91.5 along with smaller CCT value of 4,496 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Indonesian Journal of Electrical Engineering and Computer Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.