Abstract
Composite carbon molecular sieve membranes (c-CMSM) were prepared in a single dipping–drying–carbonization step from phenolic resin solutions (12.5–15wt.%) loaded with boehmite nanoparticles (0.5–1.2wt.%). A carbon matrix with well-dispersed Al2O3 nanowires was formed from the decomposition of the resin and dehydroxylation of boehmite. The effect of the carbon/Al2O3 ratio on the porous structure of the c-CMSM was accessed based on the pore size distribution and gas permeation toward N2, O2, CO2, He, H2, C3H6 and C3H8. c-CMSM with higher carbon/Al2O3 ratios had a more open porous structure, exhibiting higher permeabilities and lower permselectivities. c-CMSM performance was above the upper bound curves for polymeric membranes for several gas pairs, particularly for C3H6/C3H8 (permeability toward C3H6 of 420 barrer and permselectivity of 18.1 for a c-CMSM with carbon/Al2O3 ratio of 4.4).Unsupported films were also prepared (carbon/Al2O3 ratio 7.3) and crushed into small flakes. Equilibrium isotherms of H2, N2, O2, CO2, C3H8 and C3H6 at 293K were determined on these flakes to obtain the kinetic and adsorption selectivities toward gas pairs of interest; obtained adsorption and diffusion coefficients accurately predicted the permeabilities of all studied gases except CO2 (experimental and predicted permeabilities of 1148 and 154 barrer, respectively).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.