Abstract
Thin films of yttrium oxide doped separately with Eu 3+, Tb 3+ and Tm 3+ were deposited by spray pyrolysis. The effect of preparation conditions on the structural and cathodoluminescent (CL) properties of the thin films was investigated. Films containing Eu 3+, Tb 3+ and Tm 3+ emitted red, green and blue colors, respectively. Films of yttrium oxide doped with Tm were evaluated in detail. The blue emission of these films had CIE chromaticity coordinates of x=0.158 and y=0.150 with a dominant wavelength of 476 nm and a color purity of 78% compared to CIE Standard Source C. The CL intensity of the films under 5 kV beam excitation and a current density of 5 mA/cm 2 depended strongly on annealing conditions and thulium doping concentration. For Tm-doped films the maximum luminance was 30.4 cd/m 2 and there was a linear relationship between the CL intensity and excitation voltage. A luminance of 255 cd/m 2 was obtained for the Eu-doped film. The dominant wavelength was 604 nm with 100% purity, and x=0.645 and y=0.357. The luminance for the Tb-doped film was 72 cd/m 2 with a dominant wavelength of 547 nm and 77% purity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.