Abstract
Biosorption experiment from aqueous solutions containing known amount of rare earth elements (REEs) using pre-treated Buccinum tenuissimum shell was explored to evaluate the efficiency of shell biomass as sorbent for REEs. In this work, four kinds of sieved shell samples: (a) “Ground original sample”, (b) “Heat-treatment (480°C, 6 hours) sample”, (c) “Heat-treatment (950°C, 6 hours) sample” and (d) “Heat-treatment (950°C, 6 hours) and water added sample” were used. Furthermore, to confirm the characteristics of the shell biomass, the crystal structure, the surface morphology, and the specific surface area of these shell samples were determined. Consequently, the following matters have been mainly clarified. (1) The crystal structure of the shell biomass was transformed from aragonite (CaCO3) into calcite (CaCO3) phase by heat-treatment (480°C, 6 hours); then mainly transformed into calcium oxide (CaO) by heat-treatment (950°C, 6 hours), and calcium hydroxide (Ca(OH)2) by heat-treatment (950°C, 6 hours) and adding water. (2) The shell biomass showed excellent sorption capacity for lanthanides. (3) Adsorption isotherms using the shell biomass can be described by Langmuir and Freundlich isotherms satisfactorily for lanthanides except “heat-treatment (950°C, 6 hours) sample”. (4) Shell biomass (usually treated as waste material) can be an efficient sorbent for lanthanides in future.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.