Abstract
Multiblock poly(ether ester urethane)s comprising of poly(lactic acid) (PLA), poly(ethylene glycol) (PEG), and poly(propylene glycol) (PPG) segments were synthesized, and their aqueous solutions exhibited thermogelling behavior at critical gelation concentrations (CGC) ranging from 7 to 9 wt%. The chemical structures and molecular characteristics of the copolymers were studied by GPC, 1H NMR, 13C NMR and FTIR. The thermal stability of the poly(PEG/PPG/PLA urethane)s was studied by thermogravimetry analysis (TGA), and the PLA contents were calculated based on the thermal degradation profile. The results were in good agreement with those obtained from the 1H NMR measurements. The critical micellization concentration (CMC) of these water-soluble poly(ether ester urethane)s was determined at different temperatures using a dye solubilization method. The thermodynamic parameters for micelle formation were calculated, indicating that the process is largely entropy-driven. Interestingly, it appears that there exists a requirement for the system to possess a minimum gain in entropy before the thermogelling effect can be observed. Dilute copolymer solutions showed a lower critical solution temperature (LCST) behavior similar to pNIPAM dissolved in aqueous solutions. The thermogels hydrolytically degraded to polymer fragments corresponding to the constituent segment blocks within 3 months.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.