Abstract
AbstractStatic rechargeable zinc‐iodine (Zn‐I2) batteries are superior in safety, cost‐effectiveness, and sustainability, giving them great potential for large‐scale energy storage applications. However, the shuttle effect of polyiodides on the cathode and the unstable anode/electrolyte interface hinder the development of Zn‐I2 batteries. Herein, a self‐segregated biphasic electrolyte (SSBE) was proposed to synergistically address those issues. The strong interaction between polyiodides and the organic phase was demonstrated to limit the shuttle effect of polyiodides. Meanwhile, the hybridization of polar organic solvent in the inorganic phase modulated the bonding structure, as well as the effective weakening of water activity, optimizing the interface during zinc electroplating. As a result, the Zn‐I2 coin cells performed a capacity retention of nearly 100% after 4000 cycles at 2 mA cm−2. And a discharge capacity of 0.6 Ah with no degradation after 180 cycles was achieved in the pouch cell. A photovoltaic energy storage battery was further achieved and displayed a cumulative capacity of 5.85 Ah. The successfully designed energy storage device exhibits the application potential of Zn‐I2 batteries for stationary energy storage.image
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Similar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.