Abstract
Metalorganic chemical vapor deposition (MOCVD) GaSb growth using trimethylgallium and trimethylantimony as a function of substrate temperature and V/III ratio was examined. These parameters were found to have a significant effect on the growth rate and surface morphology of the GaSb films. A phase diagram is used to interpret the effect of these growth parameters on the GaSb film growth. The region of single-phase growth was found to be narrow, falling between 540 and 560 °C. The optimum growth conditions for the MOCVD growth of GaSb have been determined for a TMGa flow rate of 20 sccm and a carrier gas flow of 8 l/min. The optimum substrate temperature and V/III ratio were found to be 540 °C and 0.72, respectively. In these conditions the lowest hole concentration of 5 × 1016 cm-3 and the highest room temperature mobility of 500 cm2 V-1 s-1 were achieved, accompanied by a steep, well-resolved band edge at 0.72 eV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.