Atmospheric corrosion of hot and cold rolled carbon steel under field exposure in Saudi Arabia

Abstract

Carbon steel (hot and cold rolled) specimens have been exposed to the action of different atmospheres at 20 test sites distributed in Saudi Arabia and was investigated in terms of environmental factors such as average temperature, average relative humidity and deposition rates of atmospheric pollutants (Cl − and SO 2). Applying the standard ISO 9223 norm aggressiveness of the atmospheres corresponding to 0the different test sites has been determined. Calculations of corrosion rates were made via loss of weight and characterization of the corrosion products formed on samples has been carried out by means of X-ray diffraction (XRD). The major constituent of the rust formed in marine and marine-industrial environment is goethite (α-FeOOH). These samples also show the presence of a large proportion of lepidocrocite (γ-FeOOH) and small amounts of ferrihydrite and maghemite (γ-Fe 2O 3). In the case of urban and rural samples goethite is the major constituent of corrosion layers. The rust formed under the urban environment also contains large amounts of ferrihydrite and in a lesser proportion, of goethite and maghemite.