Abstract
High pressure torsion (HPT) is a well-known procedure to impart severe plastic deformation (SPD) into metallic materials. It was reported that HPT produces grain sizes finer than those using other SPD processes such as equal-channel angular pressing (ECAP). However, the application of HPT has been restricted to thin disk samples. In this study, an HPT process was developed for use with bulk samples. This process is designated as Bulk-HPT for comparison with conventional Disk-HPT. Cylindrical samples of an Al-3%Mg-0.2%Sc alloy having dimensions of 10 mm in diameter and 8.6 mm in height were prepared for Bulk-HPT. The samples were strained under a pressure of 1 GPa for 2 turns at room temperature. Microstructural observations revealed that the samples contained regions having a grain size of ~130 nm. Tensile testing showed a superplastic ductility ~480 % at 673 K with an initial strain rate of 3.3x10-2 s-1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.