Abstract
The annealing temperature dependent on the structural and magnetic properties of hematite (α-Fe2O3) powders synthesized via the sol-gel method was studied. The sol-gel method is used to prepare nanoparticles for this experiment. The annealing treatment of 200°C, 400°C, 600°C, and 800°C has been carried out to modify the physical properties. The obtained nanoparticles are characterized by their structural properties using X-ray Diffraction (XRD) and Fourier Transform Infrared (FTIR) spectroscopy. Then, magnetic properties were evaluated using Vibrating Sample Magnetometer (VSM). XRD results have shown an increase in crystallite size with an increase in annealing temperature from 35.10 nm to 60.17 nm. The increase in crystallite size can be attributed to the increase in the crystal structure’s internal energy, which promotes atomic diffusion. The FTIR results show an absorption that appears at the peak around ~530 cm-1. It indicates that the Fe3+ cation has successfully formed. The VSM results show an increase in the value of Hc with an increase in the annealing temperature from 117 Oe to 461.5 Oe. It is supported by the increase of anisotropy constant and increasing temperature annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.