Anisotropy management on microstructure and mechanical property in 3D printing of silica-based ceramic cores

Abstract

Ceramic core is an essential component in the precise casting of hollow turbine blades, and the investigation on 3D printing of silica-based ceramic cores is crucial to the development of aviation industry; however, they are suffered from difficulty in high-temperature strength and structural anisotropy. In present work, silica-based ceramic cores were prepared via DLP stereolithography 3D printing, and the anisotropy management on microstructures and properties were explored based on the particle size of fused silica powders. In 3D printed ceramic cores with coarse powders, significant anisotropy was displayed exhibiting multilayer structure with large gaps in horizontal printing and uniform porous microstructure in the vertical direction, which was further explained by the particle deposition in printing. With finer silica powders, the uniformity in the microstructures was highly improved, attributed to the enhanced particle dispersion in ceramic slurries and promoted interlayer particle rearrangement during sintering. To evaluate the anisotropy in mechanical property, the ratio of vertical strength to horizontal strength (σV/σH) was proposed, which rose from 0.48 to 0.86 as the particle size decreased from 35 µm to 5 µm, suggesting enhanced mechanical uniformity. While the average particle size of silica powders was 5 µm, the flexure strengths of ceramic cores in different directions were up to 18.5 MPa and 16.3 MPa at 1540 °C with σV/σH ratio of 0.88, which well satisfied the demands for the casting of turbine blades. This work inspires new guidance on the anisotropy management in ceramic cores prepared by 3D printing, and provides new technology for fabrication of silica-based ceramic cores with superior high temperature mechanical properties.