Abstract
Through-thickness corrosion homogeneity of stabilized AA5083 alloy thick plate was investigated. For the as-received stabilized plates, no differences in corrosion behavior are evident in the specimens from different sampling positions along the thickness direction. However, in the plates after sensitization, the specimen from the surface position (T/10, SP) exhibits the highest degree of sensitization (DoS) and stress corrosion cracking (SCC) susceptibility, indicating the through-thickness corrosion inhomogeneity. Compared with interlayer position (3T/10, IP) and center position (T/2, CP), the higher grain stored energy and richer high angle grain boundaries (HAGBs) in SP specimens promote the formation of β phases (Al3Mg2) during the sensitization process. It results in a high coverage of β phases in the SP specimen and therefore induces severe corrosion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.