Abstract
The wear process in a sliding contact results in generation of wear debris, which affects the system life. The impact depends on the wear particle properties, such as size, shape and number. In this paper, the wear particles formed during a cylinder-on-disk wear test were examined. PAO additive-free oil, steel–brass and steel–steel contact pairs were employed. A particle isolation procedure was applied, and SEM/EDS analysis was used to validate it. DLS measurements indicated the wear particles radius to be in the range from 230 to 260 nm for both materials under applied nominal pressures from 87 to 175 MPa. AFM data revealed the wear particles size to be in the range from 133 to 175 nm. A slight increase in particles size with load was observed by AFM for both materials and confirmed by DLS for steel samples. AFM measurements were taken to determine thickness, length and width distributions of the wear particles. The number of wear particles per sliding distance and per unit load was estimated to be in the range from 150 to 750particlesmmN for steel and approximately 1600–1900 particlesmmN for brass.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.