Abstract
Abstract Continuous cooling transformation diagrams were plotted for a microalloyed steel in dilatometric tests at different cooling rates, and maximum and minimum cooling rates for bainite formation were determined. Austenite grain and bainite packet sizes were measured in three bainitic microstructures obtained by continuous cooling from austenitisation temperatures of 950, 1 050 and 1 150 °C, respectively. The results show that bainitic packet growth cannot exceed the austenite grain boundaries where it has nucleated. V(C, N) particle size was measured using field emission gun scanning electron microscopy and transmission electron microscopy, respectively. Both techniques yielded very similar values, but transmission electron microscopy is preferable due to its higher resolution and the possibility to carry out electron diffraction and dispersive X-ray analyses. The presence of precipitates has contributed to raising the yield strength, which can be predicted by Orowan's expression.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.