Analysis of the adhesive interface of dentine treated with carbodiimide and chitosan before cementation of fiberglass posts with different resin cements.

Abstract

The objective of this study is to evaluate the effect of 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide (EDC) and chitosan (CHI) on the adhesive interface of resin cements to root dentine. Forty-five upper canines were sectioned, endodontically treated, prepared and divided into three groups according to dentine treatment (distilled water-DW, CHI 0.2% and EDC 0.5) and in three subgroups according to resin cement: RelyX ARC, Panavia F 2.0 or RelyX U200. Slices were obtained, with five slices of each third submitted to the analysis of the adaptation of the adhesive interface through scores and the perimeter with gaps in confocal laser scanning microscopy and one slice of each third later evaluated qualitatively in scanning electron microscopy. The results were analyzed using with Kruskal-Wallis and Spearman correlation tests. There was no difference in adaptation for the different resin cements (p = .438). EDC presented better adaptation when compared to the groups treated with DW and CHI (p < .001), while the CHI and DW presented similar adaptation values (p = .365). No difference was observed in the perimeter referring to the gap areas for the different resin cements (p = .510). EDC showed a lower percentage of perimeters with gaps when compared to CHI (p < .001), with the percentage of perimeter with gaps of teeth treated with CHI being lower than DW (p < .001). A positive correlation coefficient equal to 0.763 was obtained between the perimeter with gaps and the adaptation data of the adhesive interface (p < .001). EDC resulted in better adaptation of the adhesive interface and a lower percentage of perimeters with gaps compared to chitosan.