Abstract
Abstract In the present study, the influence of both TiO 2 nanoparticle addition and cooling rate on the melting temperature, microstructure, and mechanical behaviour of Sn3.5Ag0.5Cu (SAC) solder alloys was studied. The composite solders were prepared by mechanical mixing of TiO 2 nanoparticles with SAC solder. With the addition of TiO 2 nanoparticles into the eutectic SAC alloy, a novel SAC composite solder was successfully prepared. The melting temperature for the SAC composite solders was found to be only 1.56 °C higher than that of the SAC solder, indicating that the novel SAC composite solder is fit for existing soldering process. The cooling rate and TiO 2 nanoparticle addition affected the solidification of the microstructure dramatically. Notably, SEM observation of the microstructure of the SAC composite solders under the rapid-cooled condition revealed fine dot-like nano-Ag 3 Sn IMC in the solder matrix. The ultimate tensile strength (UTS), 0.2% yield strength (0.2YS), and microhardness of the SAC composite solder increased with the increase of TiO 2 nanoparticle content by 0.25–1.0 wt.% and the cooling rate, which could be attributed to the dispersion strengthening mechanisms. However, the ductility of the composite solders was found to decrease because of microporosity at the Ag 3 Sn network grain boundary.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.