Abstract
The interactions between oxidised tantalum and methylene diphenyl diisocyanate (MDI) have been investigated by X‐ray photoelectron spectroscopy (XPS) and time of flight secondary ion mass spectrometry (ToF‐SIMS). Thin (approximately 2 nm) and thick layers of polymeric MDI were deposited on tantalum; one set was cured at 200°C, the other dried at ambient temperature (20°C). The thick layers serve as a characteristic pMDI layer, and thin layers contain information relating to the nature of interfacial bonding. By careful fitting of the N1s region contributions relating to interfacial bonding have been established. All spectra show an Nδ+ contribution indicative of acid–base bonding; in the case of the thick films, this is of an intermolecular nature whereas in the thin films, the more intense contribution is a result of such forces between pMDI and substrate. This is confirmed by ToF‐SIMS. A lower binding energy component at ca 396 eV on the air‐dried thin layer of pMDI is the result of a formal reaction between pMDI and tantalum yielding a nitride‐like species in the N1s spectrum.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.