Abstract
Nickel-based superalloy grade IN738 has superior creep resistance, however, oxidation resistance is the main limitation of this alloy for practical applications at high temperature. Coating of nickel aluminide compounds which have high oxidation resistance on the IN738 alloys surface can remarkably increase the oxidation resistance by formation of Al 2 O 3 film as protective layer. Aluminizing by powder liquid coating methods is applied in this research. Mixed slurries of Al and Al 2 O 3 powders are pasted onto IN 738 samples and heated at 1273 K in argon atmosphere for 3.6 to 14.4 ks (1 to 4h). Slurries can be classified into four different ratios of Al: Al 2 O 3 : 10: 0, 7: 3, 5: 5 and 3: 7. The microstructure was investigated by scanning electron microscope (SEM) and optical microscope. Phases in the coated layer are characterized by Glancing Incident-angle X-ray Diffractometer (GIXD) and Electron Probe Micro Analysis (EPMA). The results show that the coated layer is formed by dissolution of nickel into liquid aluminum at aluminizing temperature resulting in formation of intermetallic compound layer. The coated layer consists of Ni 2 Al 3 as a main phase with small amount of NiAl 3 and AlCr 2 . AlCr 2 exists mostly at the layer adjacent to the top surface. For 8.1 and 14.4 ks (2.25 and 4 h) holding time, formation of AlCr 2 at the interface of matrix and coated layer occurs due to diffusion of aluminum from coated layer into nickel matrix. The effect of time shows that longer aluminizing time leads to formation of a uniform coated layer. The Al: Al 2 O 3 ratio of either 10: 0 or 7: 3 will create a uniform coated layer with thickness more than 200 μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.