Abstract
Surface modifications have been progressively applied in order to improve the mechanical, biological and chemical properties of metallic dental and orthopedic implants. Therefore, the novel and multifunctional biocomposites coating matrices, which also consist of local and targeted drug delivery systems, are the most recent applications in the medical field. In this study, gentamicin antibiotic containing HAp bioceramics were utilized in a biodegradable poly-lactic acid thin film matrix which was applied to Ti6Al4V metallic implant surfaces. nanoindentation and scratch test methods were applied. It was observed that, bonding between coating and the substrate is strong enough to be used in implant applications. Additionally, it was observed that the hardness and young modulus values of uncoated Ti6Al4V disc which were 4.3 and 125.2 GPa, respectively. However, under the same testing conditions, it was also observed that the H values (0.6-0.8GPa) and the E (50-60 GPa) values of PLA-HAp biocomposite coated samples are slightly higher than the H values (0.4-0.6 GPa) and the E values (40-50GPa) of only PLA coated sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.