Abstract
The optimum composition ratio of the anode cermet (Ni-GDC) for solid oxide fuel cells (SOFCs) varies because the electron-collecting mechanism is different depending on its applications. A Co-sputtering method facilitates ratio control with sputtering power adjustment. However, there is a practical issue with fabricating anode cermet with various ratios attributed to the large sputtering yield gap of the metal target, Ni, and the ceramic target, gadolinia-doped ceria (GDC). Therefore, in this study, a Gd-Ce metal alloy was applied instead of GDC to match the sputtering rate with that of Ni, which enables a wide ratio range achievement. A thin film of Gd-Ce oxidized after deposition and successfully transformed to crystallized GDC under a SOFC operation environment. X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) confirmed its crystallinity, and the film deposited with various power ratios was sputtered on the ScSZ electrolyte pellet to clarify the optimum Ni-GDC ratio for thin-film SOFCs. Last, the Ni-GDC was applied to anodized aluminum oxide (AAO)-supported SOFCs to maximize the performance. The performance change according to the thickness of Ni-GDC was identified, and the best performance among them was 638 mW/cm2 at 500 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.