Abstract
Low-binder eco-efficient concretes and carbon uptake are opportunities for mitigating CO2 emissions and reaching net zero goals. However, the risk of corrosion induced by carbonation can accelerate. Here, a meta-analysis of the results of corrosion current density (icorr) obtained from steel embedded in carbonated concrete was conducted considering the characteristics of concrete and environment. The literature review shows higher values of icorr than expected and reported in reference studies and standards at different exposure classes of relative humidity (RH). High levels of icorr were found in low- and high-binder-content concretes, different paste volumes, or estimated porosities. The concrete resistivity, which is less known, shows the best relationship with icorr in carbonated concrete. Resistivity reflects better moisture content, and pore saturation conditions at the steel-concrete interface than the external RH, although seldom reported. Research on the relationship between icorr during the propagation period, carbonation degree, microstructure, residual alkalinity, and resistivity for low-binder concretes is still scarce and needed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.