A substitution-based method for chromium (III) leaching from chromium-tanned leather waste (CTLW) without destroying the collagen matrix was proposed. The leaching efficiency of Cr (III) from CTLW using different organic salts was investigated and sodium oxalate (OA-2Na) was considered to be the best Cr leaching agent. The effects of leaching time, temperature, pH, concentration, shaking speed and leather thickness on Cr leaching rate were investigated and a Cr leaching rate of 98% was obtained. Thermodynamic parameters (ΔG0 < 0, ΔH0 > 0 and ΔS0 > 0) were obtained in this study. The kinetic data fitted well with the first-order kinetic equation. The apparent activation energy (Ea = 82.9563 kJ/mol) and the frequency factor (A = 2.96 × 1011) were obtained. The collagen matrix remained intact after Cr leaching by the characterization of SEM and FTIR. A substitution mechanism was proposed that Cr (III) in CTLW was complexed with oxalate and dissociated from the collagen matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.