A New Morphological Variant of Bainite

Abstract

A morphological variant of bainite unlike any other previously reported variant was observed. The new phase showed equiaxed grains often with internal radial lines. Isothermal transformation kinetics were measured and the transformation rates were observed to be very high for the initial 80% of the reaction. Transformation was accompanied by considerable recalescence and the recalescence increased with decreasing temperature. An activation energy analysis was performed using the measured isothermal transformation kinetics and an average activation energy of 42 kJ mol−1 was calculated. With the aid of a SEM and a STEM the new phase was characterized to be bainitic. Résumé Une variante morphologique de la bainite, différente de celles prélablement rencontrées, a été observée. La nouvelle phase présente des grains équiaxes avec la plupart du temps, des lignes radiales internes. Les cinétiques de transformations isothermes ont été mesurées et les taux de transformation apparaissent très élevés lors du premier 80% de la réaction. La transformation est accompagnée d'une recoalescence importante qui est d'autant plus grande que la température est abaissée. Une analyse de l'énergic d'activation a été réalisée au moyen de mesures de cinétiques de transformations isothermes et une énergie moyenne d'activation de 42 kJ mol−1 a été calculée. La nouvelle phase a été caractérisée comme étant bainitique par microscopie électronique à balayage et en transmission.