Abstract
Abstract Two types of photocatalytic films, macroporous TiO 2 -P25 (Degussa) composite films (PPMSGF-PEG) and macroporous TiO 2 films (TiO 2 -PEG), have been synthesized by a P25-PEG modified sol–gel method and a PEG modified sol–gel method, respectively. The physicochemical properties, including thermal behavior, surface morphology, crystallinity, crystal size, specific surface area (BET), pore volume and adhesion on the stainless steel substrate, of the two types of films were investigated by TGA, SEM, XRD, Raman spectroscopy, HRTEM, N 2 adsorption and the tape test. The photocatalytic activities of the films were compared using 4-chlorobenzoic acid (4-CBA) as a model organic contaminant in water. It was found that adding 10 g/L P25 in the sol can improve not only the amount of crystalline material immobilized on the support, but also the BET surface area and pore volume of the films calcined at temperatures between 500 and 600 °C. N 2 adsorption results suggested that the enhanced BET surface area and pore volume were due to the formation of large pores induced by the presence of P25 powders, which could help retain a relatively high pore volume during calcination at higher temperatures. The results on photocatalytic degradation of 4-CBA showed that the increase in photocatalytic activity caused by P25 powders reached maximum for PPMSGF-PEG calcined at 500 °C, compared with that of TiO 2 -PEG film. The tape test showed that adding 10 g/L P25 in the sol did not affect the critical calcination temperature (i.e., 500 °C) at or above which excellent adhesion between the films and the stainless steel substrate can be maintained. This study proves that optimizing calcination temperature is still an important strategy for the preparation of macroporous TiO 2 -P25 composite films with enhanced photocatalytic activity and excellent adhesion on the stainless steel substrate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.