Abstract
The susceptibility of a duplex stainless steel UNS S31803 to thermal embrittlement at 475 °C was evaluated by means of mechanical tests (impact energy and hardness), magnetic measurements (hysteresis and thermomagnetic analysis) and scanning electron microscopy. The results show that the material undergoes severe embrittlement and hardening in the first 100 h. The corrosion resistance of the ferrite phase in a 10%HNO3 + 0.05%HF solution deteriorated after 500 h of ageing. The Curie temperature (Tc) was the most sensitive magnetic property to the microstructural changes that promote embrittlement. Tc increases with ageing time due to the progressive reduction of chromium in the Fe-rich matrix during spinodal decomposition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.