Abstract
A porous reaction bonded silicon carbide (RBSC) was fabricated by a molten Si infiltration method. The porosity and flexural strength of porous RBSC fabricated in this study were dependent upon the amount of carbon source used in the SiC/carbon preform as well as the amount of Si infiltrated into the SiC/carbon preform. The porosity and flexural strength of porous RBSC were in the range of 20 vol.~49 vol.% and 38~61㎫, respectively. With increase of carbon contents and molten Si for infiltration, volume fraction of the pores was gradually decreased, and flexural strength was increased. The porous RBSCs fabricated with the same amount of molten Si show less residual Si around neck with increase of carbon source, as well as a new SiC was formed around neck which resulted in the decreased porosity and improvement of the flexural strength. In addition, decrease of the porosity and increase of the flexural strength were also obtained by increase of the amount of molten Si with the same amount of carbon source. However, it was found that the flexural strength of porous RBSC depends on the porosity rather than the amount of the newly formed SiC in neck phase between SiC particles used as a starting material.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.